Semi-silicon refractory brick is an important refractory material. Они используют полугодие глину в качестве основного сырья. У них хорошая рефрактерность, термическая стабильность, и сопротивление шлака, and are relatively low in cost. Production requires attention to raw material selection, preparation process, high-temperature sintering, and quality control. They are widely used in steel, химический, building material,s and non-ferrous metal smelting.

Composition of semi-silicon refractory brick

Composite of silica and alumina: The main components of semi-silica bricks include 60% к 75% silica and 15% к 30% alumina.

Characteristics of semi-silica brick

огнеупорный: The refractoriness of semi-silica bricks is usually between 1580°C and 1680°C.

Устойчивость к химической эрозии: It has good erosion resistance to acidic and alkaline slags.

Thermal stability: It has good thermal stability and is suitable for environments with large temperature fluctuations.

Application of semi-silica refractory brick

The volume of semi-silicon bricks is stable at high temperature (slightly expanded), which is beneficial to improve the integrity of the masonry and reduce the erosion of slag on the masonry; when in contact with high-temperature slag, a layer of glaze-like substance with high viscosity is formed on the surface of the brick, blocking the pores and preventing the slag from penetrating into the brick, thereby improving the brick’s anti-erosion ability; and the load deformation starting temperature is relatively high; so in some occasions, its service life is not inferior to that of general clay bricks. Semi-silicon refractory brick is mainly used as linings of steel ladle and refractory layers of pouring steel systems. Кроме того, they can also be used for hot furnace roofs, regenerator checker bricks, ironmaking furnace linings, various kiln furnace bottoms, and flues.