Nozzle Brick/

Fire Resistant Nozzle Brick

Product advantages: High quality and competitive price

Supply advantage: Fully automatic intelligent refractory production line

Certification: We have been approved by ISO9001/ISO14001 Sample: Sample testing is available

After Sales Service: 7*24 hours responsive customer online service, fast delivery service worldwide.

Customization: Customized refractory materials and solutions according to customer requirements.

  • Product Details
  • Inquiry

The nozzle brick is made of high-purity raw materials, formed by vibration casting and low-temperature baking, and has the advantages of high thermal strength, thermal shock resistance, corrosion resistance and erosion resistance, and thermal repair.

Introduction to nozzle brick

fire resistant nozzle brick
fire resistant nozzle brick

The seat brick is a refractory brick built at the bottom of the steel drum to fix the nozzle brick. Its shape is square, so it is also called a square brick. The seat brick is used to fix the position of the water outlet; it is convenient for dismantling and installing the water outlet; it supports the lower end of the stopper rod when pouring; after pouring, ensure that the stopper rod slides along the arc surface to the water outlet, and then cuts off the injection flow. Seat brick materials can be divided into clay, high alumina, or unfired high alumina.

Specification of fire-resistant nozzle brick

Chromium Fused AluminaFused AluminaCorundum Spinel
Al2O3  %≥90≥92≥80
Al2O3+MgO  %//≥92
Cr2O3  %≥2//
Bulk density  g/cm3≥3.0≥2.95≥2.95
Cold Crushing Strength   MPa≥60≥50≥50
0.2MPa Refractoriness under load ℃≥1700≥1700≥1700

Characteristics of nozzle brick

nozzle brick
nozzle brick
  1. High-temperature corrosion resistance
    Refining ladles have very strict requirements in terms of temperature and time, and the maximum temperature often reaches above 1750 ℃. During the refining operation, the alkalinity of the slag has a great influence on the life of the refractory material. The alkalinity of ladle refining slag varies within the range of approximately 0.6 to 0.4, so refractory materials are corroded by acidic slag, and alkaline slag with strong permeability at high temperatures is damaged quickly.
  2. High-temperature wear resistance
    Various ladle refining methods use forced stirring, which causes serious wear and tear on the nozzle brick at high temperatures.
  3. Peeling resistance
    Due to the intermittent operation, the temperature will change greatly, which is prone to thermal spalling and structural spalling, and the use conditions are very harsh. There is a big gap between the performance of the currently used steel-clad breathable bricks and the performance they should have. For example, in terms of high-temperature corrosion resistance and spalling resistance, especially the spalling resistance needs to be improved.