실리콘 카바이드 내화물 벽돌

Our factory supplies high-quality silicon carbide refractory brick. Silicon carbide brick is a high-grade refractory made of SiC as the main raw material. It has a series of excellent properties, such as high strength at room temperature and high temperature, high thermal conductivity, small linear expansion coefficient, good thermal shock resistance, excellent high-temperature abrasion resistance, strong chemical corrosion resistance, 등. It has been widely used in the fields of iron and steel, colored metallurgy, chemistry, 전기, 세라믹, and aerospace.

Silicon carbide brick types

Silicon carbide bricks can be divided into oxide bonding (clay bonding, mullite bonding, SiO2 bonding), nitride bonding (Si3N4 bonding, Sialon bonding), and self-bonding according to the bonding mode（ β- SiC bonded and recrystallized silicon carbide) and siliconized reaction sintered silicon carbide bricks.

Technique Data of silicon carbide brick

（1）Oxide Bonded Silicon Carbide Brick

품목	Specifications
	Clay Bonded SiC	Mullite Bonded SiC	SiO2 Bonded SiC
SiC %	＞85	＞70	≥90
Bulk Density g/cm3	2.5~2.6	2.55~2.65	2.6~2.7
겉보기 다공성 %	≤20	≤16	≤15
CCS MPa	≥100	≥100	≥120
CMOR MPa	≥20	≥25	≥25
Thermal Expansion Coefficient℃-1 20~1000℃	4.6×10-6	4.6×10-6	4.7×10-6
Thermal Conductivity W/(m·K) 1000℃	≥11	≥11	≥13

（2）Nitride Bonded Silicon Carbide Brick

품목	Specifications
	Si3N4 Bonded SiC	Si3N4 Bonded SiC	Sialon Bonded SiC
SiC %	≥70	≥72	≥71
Si3N4  %	≥20	≥20	/
N %	/	/	≥5.5
알2영형3  %	/	/	≥5
철2영형3  %	≤1.0	≤0.7	≤0.7
Bulk Density g/cm3	≥2.60	≥2.65	≥2.65
Apparent Porosity %	≤18	≤16	≤16
CMOR MPa	≥40	≥45	≥45
HMOR MPa 1400℃	≥40	≥45	≥45
CCS MPa	≥150	≥160	≥150
Thermal Conductivity W/(m·K) 1000℃	≥15.5	≥16	/

（3）Self-bonding Silicon Carbide Brick

품목	Specifications
	β-SiC Bonded SiC	Recrystallized SiC
SiC %	≥94	≥99
Bulk Density g/cm3	≥2.63	≥2.65
겉보기 다공성 %	≤17	≤15
CMOR MPa	≥30	≥90
HMOR MPa 1400℃	≥30	≥90
CCS MPa	≥140	≥300
Thermal Expansion Coefficient ℃-1 20~1000℃	5.5×10-6	4.8×10-6
Thermal Conductivity W/(m·K) 1000℃	≥12	≥20

（4）SiSiC Brick

품목	Specifications
SiC %	≥80
Si %	12~18
Bulk Density g/cm3	≥3.0
겉보기 다공성 %	≤0.5
CMOR MPa	≥220
HMOR MPa 1400℃	≥240
CCS MPa	≥800
Thermal Expansion Coefficient ℃-1  20~1000℃	4.5×10-6
Thermal Conductivity W/(m·K) 1000℃	≥40

Silicon carbide brick application

Silicon carbide bricks are refractory materials made of SiC as the main raw material. Containing SiC72%~99%. It is divided into clay-bonded, Si3N4 bonded, Sialon bonded, β-SiC bonded, Si2ON2 bonded, and recrystallized silicon carbide bricks. Silicon carbide bricks have high thermal conductivity and good wear resistance, 열충격 저항, and corrosion resistance. It can be used for aluminum electrolytic cell linings, molten aluminum conduits and kiln furniture for ceramic kilns, lower parts of large and medium-sized blast furnaces, waists and belly, aluminum refining furnace linings, zinc distillation tank linings, 등.