Submerged Entry Nozzle

A submerged entry nozzle can protect the molten steel from oxidation when it flows into the crystallizer from the tundish, evenly distribute the molten steel into the crystallizer, and control the flow state of the molten steel in the crystallizer, with good slag resistance, anti-blocking, long service life, and low accident rate.

Technical parameter of erosion resistance submerged entry nozzle

Physical and chemical indicators：

Artikal	Indeks
Artikal	JSK55	JSK50	JSK45	JSK40
Al₂O₃ %	≥55	≥50	≥45	≥40
C %	≥16	≥18	≥20	≥22
Flexural Strength MPa	≥5.5	≥5.5	≥5.5	≥5
Apparent porosity %	≤19	≤19	≤19	≤19
Bulk density g/cm³	≥2.36	≥2.32	≥2.28	≥2.18

Slag Area：

Artikal	Indeks
Artikal	Z75	Z70	Z65	Z55
ZrO₂ %	≥75	≥70	≥65	≥55
C %	≥9	≥12	≥15	≥18
Apparent porosity %	≤21	≤21	≤21	≤22
Bulk density g/cm³	≥3.6	≥3.5	≥3.4	≥3.2

The main functions of the submerged nozzle

(1) Prevent secondary oxidation and nitridation of molten steel and splashing of molten steel;
(2) Regulate the flow state and injection speed of molten steel;
(3) Prevent non-metallic inclusions in protective slag from being drawn into molten steel, which plays an important role in promoting the floating of inclusions in molten steel;
(4) It has a decisive influence on the yield rate of side casting and the quality of the ingot.

The production process of submerged nozzle

The manufacturing process of the submerged nozzle is as follows: various raw materials are kneaded to form a uniformly mixed composite powder, which is isostatically pressed to form a green body of the required shape, which is sintered at high temperature to form a product with a certain strength, and then shaped to the required size. Finally, after inspection, it is packaged and shipped out.