Aluminum Magnesium Carbon Brick

Alumina magnesia carbon brick has the advantages of corrosion resistance, spalling resistance, good resistance to molten steel scouring, safe use, less steel and slag, easy unpacking, and so on.

AMC refractory brick introduce

Alumina-magnesia carbon bricks, referred to as AMC bricks, are unburned refractory bricks made from raw materials such as magnesia, high-aluminum aggregates, and carbon materials through crushing, mixing, shaping, and drying processes.

Parameter of aluminum magnesium carbon brick

Indeks Artikal		RS-A	RS-80	RS-85	RS-88
MgO	%	86	85	88	90
Al2O3	%	5	7	6.5	6.5
SiO2	%	3.2	4	2.4	1.2
CaO	%	1.6	1.5	1.3	1.2
Fe2O3	%	3.7	1.7	1.4	1.0
Apparent Porosity	%	16~20	17	17	17
Density Bulk	g/cm3	2.85~3.0	2.93	2.93	2.94
Cold Crushing Strength	Mpa	41	50	50	55
0.2Mpa Under Load Refractoriness	℃	≥ 1550	1610	1650	1700
Thermal Shock Resistance(1100℃,water,quenching, cycle)		3~6	3~6	3~6	3~6

Alumina-magnesia carbon brick application

Alumina-magnesia carbon bricks have the advantages of corrosion resistance, spalling resistance, balanced erosion, safe use, less steel and slag staining, and easy unpacking. Alumina magnesia carbon fire brick for the steel ladle is mainly used for the lining of steel used in harsh conditions. Refractory alumina magnesia carbon bricks for the steel ladle used in the molten pool part and the bottom part of the continuous casting large tundish and the refining package outside the furnace.