Effect of different graphite content on magnesia carbon refractory bricks

Magnesia carbon refractory bricks are an alkaline refractory material made of magnesia and graphite as raw materials and using various binders. As an important component of magnesia-carbon refractory materials, graphite content has a crucial impact on the performance of magnesium-carbon refractory materials. Due to the high thermal conductivity of graphite, low thermal expansion coefficient, and non-wetting between graphite and slag.

Application of magnesia carbon refractory bricks

Magnesia Carbon Brick
Magnesia Carbon Brick

Magnesia-carbon bricks are very important refractory materials. Magnesia-carbon bricks are used in many kilns, such as the linings of various electric arc furnaces, ladles, and steelmaking refining furnaces (BOF, RH).

Direct oxidation and indirect oxidation of graphite

magnesium carbon bricks
magnesium carbon bricks

Adding graphite greatly improves the thermal shock resistance and slag erosion resistance of magnesium carbon refractory materials. However, graphite is easily oxidized, which increases the pores of magnesia carbon bricks and also leads to a reduction in strength and corrosion resistance, as well as material peeling and structural damage. Therefore, the research on the oxidation resistance of magnesium carbon refractory materials has very important practical significance.
Graphite oxidation can be divided into direct oxidation and indirect oxidation. Direct oxidation mainly refers to the reaction between graphite and oxygen; while indirect oxidation mainly refers to the reaction of graphite and magnesium oxide at high temperatures. It is generally believed that when the temperature is lower than 1400°C, direct oxidation mainly occurs; when the temperature is higher than 1400°C, indirect oxidation plays a major role.

Effect of graphite content on magnesia carbon bricks

magnesia carbon refractory bricks
magnesia carbon refractory bricks

After testing by Rongsheng Refractory Materials Company, it was found that the graphite content has the following effects on magnesia carbon bricks:

  1. The volume density of magnesia carbon bricks decreases with the increase of graphite content, and the porosity increases with the increase of graphite content. After carbonization at 900°C, the volume density of the magnesia carbon brick sample decreased, while the porosity increased significantly.
  2. The higher the graphite content in the magnesia carbon brick sample, the thinner the thickness of the decarburization layer, and the lower the graphite oxidation rate. At the same time, the decarburization layer thickness and graphite oxidation rate of magnesia carbon bricks oxidized at 1400°C are lower than those of magnesia carbon bricks oxidized at 1000°C.
  3. The oxidation rate of the magnesia-carbon brick sample was calculated using the oxidation model, its changing trend with the graphite content is relatively consistent with the actual measured change trend of the decarburized layer thickness. That is, the oxidation rate decreases with the increase of graphite content, and the decrease is most obvious when the graphite content is low.