Konstruktion aus feuerfestem Mullit-Gussmaterial

Feuerfestes Mullit-Gussmaterial wird aufgrund seiner guten Feuerbeständigkeit in Hochtemperaturindustrien bevorzugt, Thermoschockbeständigkeit, und Stärke. They are often used in high-temperature furnace linings in industries such as steel, Petrochemie, und Zement. To achieve the best use of Mullitgussteile, the correct construction method is essential. This article will introduce the construction steps and precautions of mullite castables in detail to help you understand how to ensure construction quality and use results.

Construction of mullite castable

Preparation before construction

High-strength high-alumina mullite castable is made of multiple ingredients, with active composite ultrafine powder and a small amount of pure calcium aluminate cement added. It has high activity, so the storage conditions and time requirements are high. It must be strictly prevented from moisture. If the packaging is damaged or damp, it must not be used. Its storage period should not exceed three months from the factory. Construction machinery must be cleaned to ensure the normal operation of construction machinery, such as forced mixers, vibrating rods, scales, and drilling hand drills.

Konstruktion aus feuerfestem Mullit-Gussmaterial

Vor dem Bau, operators should master each process’s key points and quality requirements. Nach Zugabe der Materialien in den Mixer, Trocken mischen und umrühren 1 Minute, und dann Wasser hinzufügen. If the materials are too dry or too thin, the quality will be affected. It is OK to knead them into a ball and make a slurry. Es ist strengstens verboten, beim Ausgießen aus dem Tank vorübergehend Wasser hinzuzufügen. Sobald die Wassermenge bestimmt ist, Es sollte nicht einfach geändert werden, um sicherzustellen, dass die Dichte jeder Mischung konsistent ist. Die empfohlene Mischzeit beträgt 5 Minuten. It is not good to be too long or too short. Der angemischte Guss sollte sofort gegossen werden, und die Parkzeit sollte nicht überschritten werden 20 Minuten.
Der Beton muss auf der Baustelle gleichmäßig verlegt werden. Do not use too much force to dislocate the formwork, Erweiterungsplatte, Ankersteine, and other facilities. Allgemein, the material is vibrated with a vibrator after about 300mm of laying, and each part should be returned to the slurry. When pulling out the vibrator, it should be lifted slowly to avoid leaving holes. If it is found that there is no vibration, es sollte ausgegraben und erneut gerüttelt werden. Nach dem Gießen, die Oberfläche des Gusskörpers muss nicht geglättet werden.
Natürliche Heilung für 2 Zu 3 Tage. Während der Aushärtezeit, it is strictly forbidden to step on or touch the castable. Wenn das Gießmaterial erstarrt, vent holes should be made in time to help remove water vapor. Demolding can be done only after it is confirmed to have sufficient strength.

Mullite castable baking

High-strength and high-aluminum mullite castables are dense and high-strength, with very low porosity, und es ist nicht einfach, Wasser reibungslos zu entfernen. Besonders in der Phase der Entfernung einer großen Menge freien Wassers im Temperaturbereich von 100-300 ℃, Es kann leicht zu einem übermäßigen Dampfdruck und zum Abblättern der Auskleidung oder zu Explosionsunfällen kommen, so special attention should be paid and sufficient removal time should be given. As the temperature rises, free and crystal water are continuously removed. Wenn es erreicht 500 ℃, Der Wassergehalt des Gussmaterials beträgt nur ca 10% of the total water content. daher, the castable should be heated slowly before 600 ℃ and have sufficient insulation time. After 1000 ℃, Es beginnt sich in großen Mengen Mullit zu bilden, and the formation of mullite primary crystals is basically completed at 1300 ℃. As the mullite grains continue to grow, the castable becomes dense, the bonding force increases and the strength continues to increase.