Fused corundum bricks are made by melting alumina in an electric arc furnace and casting it into a model of a specified specific shape. After annealing and heat preservation, the required product is obtained by processing with diamond abrasive tools.

Introduction to three types of fused corundum bricks

Fused α-corundum brick is mainly composed of α-Al₂يا₃, which has high-temperature resistance, strong alkali resistance, compact structure, excellent chemical stability, strong wear resistance, and is far more resistant to various slags than other aluminum silicates. It is an ideal material for metallurgical electrolytic cells and sliding rail bricks for heating furnaces.
Fused β-corundum bricks are mainly composed of β- آل₂يا₃, with dense structure and strong spalling resistance, especially showing extremely high corrosion resistance to strong alkali vapor, no pollution to molten glass, and are used for upper structures with less glass raw materials scattered.
Fused α-β corundum brick is composed of about 50% of α- آل₂يا₃and β- آل₂يا₃. The two crystals interlace to form a dense structure, which has excellent alkali resistance, and the corrosion resistance of molten glass is comparable to that of AZS bricks and does not pollute the glass liquid. , Mainly used for high-grade glass furnaces working pool walls and pavement, forehearth and passage, إلخ.

Technical Parameter of Fused Corundum Brick

غرض	فِهرِس
غرض	Fused Cast α Corundum Bricks	Fused Cast β Corundum Bricks	Fused Cast α-β Corundum Bricks
آل₂يا₃ %	98	92	94.0
Na₂يا %	1.0	6.5	4.0
شافي₂+CaO+Fe₂يا₃+تيو₂ %	.01.0	≤1.5	.02.0
α-Corundum %	90	2	44
β-Corundum %	4	97	55
Glass Phase %	6	1	1
الكثافة الظاهرية (جزء كثيف) جم / سم³	3.3	3.1	3.3
Cold Crushing Strength MPa	200	50	200
0.2Mpa Refractoriness Under Load ℃	1700	1700	/
Static Resistance To Liquid Glass Erosion Depth mm/24h Ordinary Soda Lime Glass 1350℃×48h	/	/	0.3